Are your layers modeled with solid elements as is implied by the image?
Are the layers merged together via shared nodes at each layer interface?
Do the material models include failure criteria such that elements may be deleted?
Assuming yes to all questions, *CONTACT_ERODING_SINGLE_SURFACE with all the parts on SURFA (slave side) would be appropriate.