Andreas Koutras
Hello Sami,
Note that we cannot provide recommendations on specific material stress-strain data. I cannot share the data of the MAT_PAPER above.
Here is another example.
*MAT_PAPER_TITLE
Lower 00
$# mid ro E1 E2 E3 pr21 pr32 pr31
1 1.0000E-9 7122.3200 2948.3900 14.000000 0.46 0. 0.
$ G12 G23 G13 E3C CC TWOK
1685.6900 30.000000 30.000000 0.47 24.46 4.
$ S01 A01 B01 C01 S02 A02 B02 C02
-101. 0. 0. 0. -102. 0. 0. 0.
$ S03 A03 B03 C03 S04 A04 B04 C04
$ A4=B4=C4=0 ger idealplastiskt i tryck sig=S04 i MD
24.64 5.82 117.25 865.05 39.13 0. 0. 0.
$ S05 A05 B05 C05 PRP1 PRP2 PRP4 PRP5
$ A5=B5=C5=0 ger idealplastiskt i tryck sig=S05 i CD
17.23 0. 0. 0. 0. 0. 1.E-4 1.E-4
$ ASIG BSIG CSIG TAU0 ATAU BTAU
-16.45 16.550 -3.16 2.1 9. 2.
$# aopt mafc xp yp zp a1 a2 a3
2.000000 1.000000 0.000 0.000 0.000 1.000000 0.000 0.000
$# v1 v2 v3 d1 d2 d3 beta
0.000 0.000 0.000 0.000 0.000 1.000000 0.000
*MAT_PAPER_TITLE
Mid 00
$# mid ro E1 E2 E3 pr21 pr32 pr31
2 1.0000E-9 4029.2000 1823.5500 13.000000 0.44 0. 0.
$ G12 G23 G13 E3C CC TWOK
1023.0200 35.000000 35.000000 0.38 16.33 4.
$ S01 A01 B01 C01 S02 A02 B02 C02
-201. 0. 0. 0. -202. 0. 0. 0.
$ S03 A03 B03 C03 S04 A04 B04 C04
$ A4=B4=C4=0 ger idealplastiskt i tryck sig=S04 i MD
16.48 11.66 37.68 253.82 25.58 0. 0. 0.
$ S05 A05 B05 C05 PRP1 PRP2 PRP4 PRP5
$ A5=B5=C5=0 ger idealplastiskt i tryck sig=S05 i CD
10.93 0. 0. 0. 0. 0. 1.E-4 1.E-4
$ ASIG BSIG CSIG TAU0 ATAU BTAU
-11.78 11.880 -1.92 0.95 9. 2.
$# aopt mafc xp yp zp a1 a2 a3
2.000000 1.000000 0.000 0.000 0.000 1.000000 0.000 0.000
$# v1 v2 v3 d1 d2 d3 beta
0.000 0.000 0.000 0.000 0.000 1.000000 0.000
*MAT_PAPER_TITLE
Upper 00
$# mid ro E1 E2 E3 pr21 pr32 pr31
3 1.0000E-9 7361.5298 2788.4900 20.000000 0.48 0. 0.
$ G12 G23 G13 E3C CC TWOK
1764.0699 84.000000 84.000000 0.47 24.46 4.
$ S01 A01 B01 C01 S02 A02 B02 C02
-301. 0. 0. 0. -302. 0. 0. 0.
$ S03 A03 B03 C03 S04 A04 B04 C04
$ A4=B4=C4=0 ger idealplastiskt i tryck sig=S04 i MD
24.54 6.38 144.25 552.02 41.57 0. 0. 0.
$ S05 A05 B05 C05 PRP1 PRP2 PRP4 PRP5
$ A5=B5=C5=0 ger idealplastiskt i tryck sig=S05 i CD
17.41 0. 0. 0. 0. 0. 1.00E-4 1.0E-4
$ ASIG BSIG CSIG TAU0 ATAU BTAU
-16.45 16.550 -3.16 2.7 9. 2.
$# aopt mafc xp yp zp a1 a2 a3
2.000000 1.000000 0.000 0.000 0.000 1.000000 0.000 0.000
$# v1 v2 v3 d1 d2 d3 beta
0.000 0.000 0.000 0.000 0.000 1.000000 0.000
*MAT_COHESIVE_GENERAL
$# mid ro roflg intfall tes tslc gic giic
5 1.0000E-9 1 1.000000 2.000 2 0.083800 0.174700
$# xmu t s stfsf
1.000000 0.240000 1.125000 2.00000
*DEFINE_CURVE_TITLE
TSLC
$# lcid sidr sfa sfo offa offo dattyp
2 0 1.000000 1.000000 0.000 0.000 0
$# a1 o1
0.000 0.000
0.003460 1.000000
0.400000 0.300
1.000000 0.000
*DEFINE_CURVE_TITLE
MD Tension Bottom
$# lcid sidr sfa sfo offa offo dattyp
101
$# a1 o1
0.0 39.13
5.E-3 60.169
1.E-2 72.490
1.E-1 72.490
*DEFINE_CURVE_TITLE
CD Tension Bottom
$# lcid sidr sfa sfo offa offo dattyp
102
$# a1 o1
0.0 17.230
5.E-3 23.761
1.E-2 27.890
1.5E-2 30.727
2.0E-2 33.200
2.5E-2 35.600
2.7E-2 36.540
1.E-1 36.540
*DEFINE_CURVE_TITLE
MD Tension Mid
$# lcid sidr sfa sfo offa offo dattyp
201
$# a1 o1
0.0 25.58
5.E-3 35.000
6.E-3 36.277
1.E-1 36.277
*DEFINE_CURVE_TITLE
CD Tension Mid
$# lcid sidr sfa sfo offa offo dattyp
202
$# a1 o1
0.0 10.930
5.E-3 14.410
1.E-2 16.590
1.5E-2 17.980
2.0E-2 19.110
2.5E-2 20.186
2.9E-2 21.000
1.E-1 21.000
*DEFINE_CURVE_TITLE
MD Tension Top
$# lcid sidr sfa sfo offa offo dattyp
301
$# a1 o1
0.0 42.57
5.E-3 57.470
1.E-2 67.500
1.E-1 67.500
*DEFINE_CURVE_TITLE
CD Tension Top
$# lcid sidr sfa sfo offa offo dattyp
302
$# a1 o1
0.0 17.410
5.E-3 23.430
1.E-2 27.355
1.5E-2 29.634
2.0E-2 31.200
2.5E-2 32.533
2.8E-2 33.287
1.E-1 33.287